PHIL DICKENS wrote:
> Dear Jody,
> We have had much more success with SLA moulds. We have only moulded
> polypropylene but have had tools produce over 500 parts without
> We are running a new SLA tool on Monday which is the most complicated
> I have seen yet. It is for producing a very complex comb/brush using
> a double cavity insert. The total shot weight is 0.080 kg.
> We are hoping to get 1,000 parts out of this new tool so we are
> keeping are fingers crossed.
> It really depends on the moulding machine operator. If a mistake is
> made then we have early failure.
> Phill Dickens
> University of Nottingham
> > Date: Thu, 20 Nov 1997 18:42:09 -0600
> > From: "MET-L-FLO INC." <firstname.lastname@example.org>
> > To: Ingrid Timmel <email@example.com>
> > Cc: firstname.lastname@example.org
> > Subject: Re: Tooling Resins vs. SLA
> > DEAR INGRID,
> > We did some R&D with SLA molds and found they wont last more than 5 shots in an
> > injection press with production material. The same study showed a high heat epoxy
> > mold lasted about 10 shots. If anybody has any information about this I would be
> > interested to hear it as well.
> > Best Regards to All,
> > Jody Hudrick
> > MET-L-FLO INC.
> > Ingrid Timmel wrote:
> > > What is the major advantage of making a SLA mold for injection parts over
> > > casting a mold from heat-resistant epoxy ?
> > > It takes less time to make, clean up the part and cast the mold, than it would
> > > to set up everything for making a mold from SLA.
> > > Thanks in advance.
> > >
> > > --
> > > Ingrid Timmel